Synthesis and characterization of FeTiO3 ceramics

Abstract

Nanocrystalline FeTiO3 ceramic powders were prepared by the sol–gel process combined with a surfactant-assisted template method. The resulting powders were calcined at different temperatures ranging from 150 °C to 600 °C for 2 h in air. The results revealed that a pure hexagonal phase of FeTiO3 could be obtained at a low temperature, 600 °C. The phase evolution of FeTiO3 was investigated by X-ray diffraction patterns (XRD), Fourier-transform infrared spectroscopy (FT-IR), and X-ray photoelectron spectroscopy (XPS). Particle size and morphology were studied by transmission electron microscopy (TEM).

Keywords

• Sol–gel process
• Nanoparticles
• Electron microscopy
• Ti–O bond
• Hexagonal phase