Evaluation of the antimicrobial activity of each component in Grossman’s sealer Avaliação da atividade antimicrobiana de cada um dos componentes do cimento de Grossman

Abstract

The antimicrobial activity of Grossman’s sealer and its components was evaluated on 13 different strains using the double layer well-diffusion method. Results revealed that Grossman’s sealer presented antimicrobial activity against all the tested strains. Among the components of the cement, sodium tetraborate presented the greatest antimicrobial activity, both in type and diameter of the halo and ring of inhibition. Sealer powder, rosin, and eugenol presented similar activity, with no effect on P. aeruginosa and C. albicans. Among these, only eugenol had an effect on E. coli. Zinc oxide was only active against S. sobrinus and E. coli. Barium sulfate and bismuth subcarbonate did not show any antimicrobial effect.Os autores estudaram a atividade antimicrobiana do cimento de Grossman e de seus componentes sobre 13 diferentes cepas pelo método de difusão de poço em camada dupla. Os resultados revelaram que o cimento de Grossman apresentou atividade antimicrobiana contra todas as cepas utilizadas. Dos componentes do cimento, o tetraborato de sódio foi o que apresentou maior atividade antimicrobiana, tanto por tipo como por tamanho do halo e aro de inibição. O pó do cimento, o breu e o eugenol apresentaram atividades semelhantes, sendo que eles não tiveram ação sobre P. aeruginosa e C. albicans e, dos três componentes, somente o eugenol teve ação sobre E coli. O óxido de zinco somente teve ação sobre S. sobrinus e E. coli. O sulfato de bário e o subcarbonato de bismuto não tiveram nenhuma ação antimicrobiana.

Keywords

• Microbiologia
• Materiais restauradores do canal radicular
• Microbiology
• Root canal filling materials