A green rust-coated expanded perlite particle electrode-based adsorption coupling with the three-dimensional electrokinetics that enhances hexavalent chromium removal

Abstract

A green rust-coated expanded perlite (GR-coated Exp-p) microelectrode was synthesized and incorporated into a column-mode three-dimensional electrokinetic (3D-EK) platform to effectively pursue a continuous Cr(VI) removal from the aqueous solution. Brucite-like layers of GR were decorated onto the Exp-p material. The molar ratio of Fe(II) to Fe(III) played a most vital role among the three synthesis factors in influencing the performance of the particle electrode. For the equilibrium adsorption experiments, the target maximum adsorption capacity of 122 mg/g was predicted by a target optimizer and desirability function at the conditions following the pH of 4.7, the initial concentration of 172.4 mg/L, the dosage of 0.28 g/L, and the temperature of 28.96 °C, respectively. SO42−, Cl−, and NO3− fiercely competed with Cr(VI) anions in the acidic conditions for the locally positive sites. A low concentration and a slow flow were favored in the column-mode 3D-EK platform. The pseudo-first-order and Langmuir models were suitable for describing the kinetics and isotherms of the adsorption process, respectively. Cr(VI) anions were electrostatically attracted to the silanol groups and GR surface of the adsorbent, subsequently reduced in both heterogeneity and homogeneity, and finally immobilized by coordinating with silanediol groups and silanetriol groups.

Keywords

• Green rust-coated expanded perlite
• Microelectrode
• Three-dimensional electrokinetics
• Hexavalent chromium
• Optimization
• Breakthrough curve