Boletín de la Sociedad Española de Cerámica y Vidrio (Apr 2004)

Caracterización de la aleación 2014 reforzada con intermetálicos

  • Cambronero, L. E. G.,
  • Herranz, J. D.,
  • Ruiz-Román, J. M.,
  • Ruiz-Prieto, J. M.

Journal volume & issue
Vol. 43, no. 2
pp. 291 – 293

Abstract

Read online

On the present work the objective is to manufacture a AA2014+10 vol-% Intermetallic (NbAl3 or FeAl2 ) metal matrix composites. Since Powder Metallurgy route was chosen, the powder mixtures of metallic powders which forms AA2014 alloy and intermetallic powders were obtained by mechanical alloying. Powder mixtures were cold die pressing and green samples were hot extruded. As result of this intermetallic addition, mechanical properties of AA2014 alloy are improved and a tensile strength of 516 MPa on AA2014+NbAl3 and 465MPa on AA2014+FeAl2 within an elongation close to 2% on both metal matrix composite materials are reached.<br><br>El objeto del presente trabajo es la obtención de los materiales compuestos AA2014 +10 vol-% NbAl3 o FeAl2. Para ello se realizó la mezcla inicial de los polvos metálicos que constituyen la aleación AA2014 y de los polvos de estos intermetálicos seguido de su aleación. Las mezclas obtenidas se compactaron en frío y los compactos en verde se extruyeron en caliente. Como resultado de la adición de los intermetálicos se mejoran las propiedades mecánicas de la aleación AA2014, alcanzándose resistencias a tracción de 516 MPa para el AA2014+NbAl3 y de 465MPa para el AA2014+FeAl2, con un alargamiento próximo al 2.0% en ambos materiales compuestos de matriz metálica.

Keywords