Study on preparation and performance of additive flame retardant DOPO-HQ modified epoxy composite

Abstract

An additive flame retardant was prepared from DOPO-HQ. Fourier transform infrared spectroscopy (FT-IR) was used to analyze its chemical structure. It was added to the experimental formula to prepare EP composite material, and the limiting oxygen index experiment and thermogravimetric analysis experiment were carried out on the material, and the scanning electron microscope experiment was carried out on the residual carbon after combustion. The results show that the modified epoxy resin has a limiting oxygen index of 29.5%, and there is no droplet during combustion; thermogravimetric analysis experiments show that the temperature at which the thermal weight loss is 5%wt decreases, but the residual carbon rate increases. Scanning electron microscopy (SEM) test results show that carbon layer formed by the combustion products of epoxy resin is denser..

Keywords

• additive flame retardant
• epoxy resin
• limiting oxygen index