Scientific Reports (Jun 2024)

Newly developed CeO2 and Gd2O3-reinforced borosilicate glasses from municipal waste ash and their optical, structural, and gamma-ray shielding properties

  • E. M. Abou Hussein,
  • S. E. Shaban,
  • Y. S. Rammah,
  • M. Hamed Misbah,
  • M. A. Marzouk

DOI
https://doi.org/10.1038/s41598-024-63207-4
Journal volume & issue
Vol. 14, no. 1
pp. 1 – 19

Abstract

Read online

Abstract From the useless municipal solid waste (MSW) ashes, CeO2, Gd2O3 and CeO2 + Gd2O3 doped borosilicate glasses were organized via melting-quenching procedure. Various optical, structural, physical and radiation shielding parameters were examined towards the influence of 100 kGy of γ-radiation. UV–visible NIR spectra revealed UV peaks at 351, 348 and 370 nm corresponding to the trivalent states of Ce3+ and Gd3+ ions, while, photoluminescence (PL) spectra displayed asymmetric broad excitations of Ce3+ and Gd3+ ions due to 4f → 5d transitions, and emission intense bands at 412, 434, and 417 nm. CIE chromaticity shows that Gd3+ ions increase the luminescence of Ce3+. FTIR absorption bands revealed an overlapping between tetrahedral groups of silicate (SiO4), with trigonal (BO3) and tetrahedral (BO4) units of borate. The influence of 100 kGy obtains quite reduction in UV–visible NIR and PL peaks, large stability in FTIR and ESR spectra, and stability of thermal expansion coefficient (CTE) as well. The whole data revealed optical, structural and physical stability of glasses after irradiation besides an enhancement in microhardness owing to more structural compactness and high bonding connectivity. Radiation shielding parameters from Phy-X/PSD program showed higher values of mass (MAC) and linear attenuation coefficients (LAC), and effective atomic number (Zeff) in the order of; glass Ce+Gd > glass Ce > glass Gd. Ce + Gd doped glass revealed also the lowest half value layer (HVL) comparing to other shielding commercial concretes. The study recommends the beneficial and economical use of the useless MSW ash to produce CeO2 and/or Gd2O3 borosilicate glasses with hopeful radiation shielding features.

Keywords