Improving Gamma Ray Shielding Behaviors of Polypropylene Using PbO Nanoparticles: An Experimental Study

Abstract

Recently, polymers have entered into many medical and industrial applications. This work aimed to intensively study polypropylene samples (PP) embedded with micro and nanoparticles of PbO for their application in radiation shielding. Samples were prepared by adding 10%, 30%, and 50% by weight of PbO microparticles (mPbO) and adding 10% and 50% PbO nanoparticles (nPbO), in addition to the control sample (pure polypropylene). The morphology of the prepared samples was tested; on the other hand, the shielding efficiency of gamma rays was tested for different sources with different energies. The experimental linear attenuation coefficient (LAC) was determined using a NaI scintillation detector, the experimental results were compared with NIST-XCOM results, and a good agreement was noticed. The LAC was 0.8005 cm−1 for PP-10%nPbO and 0.6283 cm−1 for PP-10%mPbO while was 5.8793 cm−1 for PP-50%nPbO and 3.9268 cm−1 for PP-50%mPbO at 0.060 MeV. The LAC values have been converted to some specific values, such as half value layer (HVL), mean free path (MFP), tenth value layer (TVL), and radiation protection efficiency (RPE) which are useful for discussing the shielding capabilities for gamma-rays. The results of shielding parameters reveal that the PP embedded with nPbO gives better attenuation than its counterpart pp embedded with mPbO at all studied energies.

Keywords

• polypropylene
• PbO nanoparticles
• SEM
• mechanical
• radiation shielding