Synthesis and Characterization of LSX Zeolite/AC Composite from Elutrilithe

Abstract

The porous carbonaceous precursor obtained from elutrilithe by adding pitch powder and solid SiO2 was employed for the first time in an in situ hydrothermal synthesis of LSX zeolite/AC composite. The synthesized samples were characterized by XRD, SEM, and N2 adsorption–desorption. The optimum conditions for the hydrothermal synthesis process were set as follows: gelling, aging, and crystallization. The time and temperature required for these steps were 24 h and 65 °C, 12 h and 20 °C, and 48 h and 65 °C, respectively. The molar ratios were (Na2O + K2O)/Al3O2 = 7.7, K2O/(K2O + Na2O) = 3. The potential applicability test of the product showed high CO2 working capacity, excellent CO2/CH4 and CO2/N2 selectivity, and high phenol adsorption capacity. These results suggest that the resultant product has excellent potential value in industrial application.

Keywords

• hydrothermal synthesis
• alkalinity
• LSX zeolite/AC composite
• gas adsorption
• wastewater treatment