In vivo performance of a rare earth free Mg–Zn–Ca alloy manufactured using twin roll casting for potential applications in the cranial and maxillofacial fixation devices

Abstract

A magnesium alloy containing essential, non-toxic, biodegradable elements such as Ca and Zn has been fabricated using a novel twin-roll casting process (TRC). Microstructure, mechanical properties, in vivo corrosion and biocompatibility have been assessed and compared to the properties of the rare earth (RE) element containing WE43 alloy. TRC Mg-0.5 wt% Zn- 0.5 wt% Ca exhibited fine grains with an average grain size ranging from 70 to 150 μm. Mechanical properties of a TRC Mg-0.5Zn-0.5Ca alloy showed an ultimate tensile strength of 220 MPa and ductility of 9.3%. The TRC Mg-0.5Zn-0.5Ca alloy showed a degradation rate of 0.51 ± 0.07 mm/y similar to that of the WE43 alloy (0.47 ± 0.09 mm/y) in the rat model after 1 week of implantation. By week 4 the biodegradation rates of both alloys studied were lowered and stabilized with fewer gas pockets around the implant. The histological analysis shows that both WE43 and TRC Mg-0.5Zn-0.5Ca alloy triggered comparable tissue healing responses at respective times of implantation. The presence of more organized scarring tissue around the TRC Mg-0.5Zn-0.5Ca alloys suggests that the biodegradation of the RE-free alloy may be more conducive to the tissue proliferation and remodelling process.

Keywords

• Mg–Zn–Ca alloy
• Twin-roll strip casting
• In vivo degradation
• Biocompatibility
• Biodegradable implants