Morphological and Structural Study of Anodized Titanium Grade 2, Using HCl in Aqueous Solution

Abstract

Abstract In this work, the electrochemical anodization process was carried out on titanium grade 2, using an electrolytic solution of 3 M and 0.15 M HCl with voltages of 11 V, 12 V and 15 V, as well as time variations in the experimental process and later an annealing process at 750 °C. According to the results obtained, the TiO2 coatings presented different morphologies on their surface, which consisted of nanopores, nanowires and clusters of oxide grains, as well as a combination of anatase and rutile crystalline phases. Band Gap variations were found to be non-significant despite changes in the morphology of the coatings at different anodization conditions, with an average value of 2.91 eV. It was observed that the anodized samples treated by the annealing process at 750 °C, thickness values up to 16 μm were obtained.

Keywords

• Electrochemical anodization
• HCl
• nanostructures
• Titanium Grade 2
• TiO2