Effect of Track Overlap on the Microstructure and Properties of the CoCrMoSi PTA Coatings

Abstract

Broadly speaking, the research and design of coatings are generally studied by way of single-track deposits; otherwise, the development of a coated part entails the understanding of how multi-track welding influences the microstructure and properties of the surface. This study evaluated the effect of track overlap on the microstructure and properties of the CoCrMoSi Tribaloy T400 alloy coatings produced on AISI 316L steel substrate. The characterization was performed by scanning electron microscopy, hardness and X-ray diffraction. The correlation between the degree of overlap and performance of the coatings was assessed by wear tests. The single track deposits showed hypoeutectic microstructure as a result of high Iron, Chromium and Nickel content. From the second track on, the chemical composition was displaced back to eutectic and then to hypereutectic with overlap of 25 and 50%, respectively. The microstructure dictated the hardness of the coatings (527 – 701 HV0.5) and the lower mass loss rate was measured for hypereutectic with primary Laves phase.

Keywords

• CoMoCrSi alloy
• plasma transferred arc
• dilution
• track overlapping
• microstructure
• wear behavior