Properties of a Pressureless Sintered 2Y-TZP Material Combining High Strength and Toughness

Abstract

Yttria stabilized zirconia materials are frequently used in mechanical engineering and biomedical applications. Demanding loading conditions require materials combining a high level of strength and fracture toughness. A ready-to-press alumina doped 2 mol% yttria-stabilized zirconia powder was shaped by axial pressing and sintering in air at 1250–1500 °C for 2 h. At 1350 °C the best combination of strength (1450 MPa) and toughness (7.8 MPa√m) was achieved. Materials sintered in the middle of the chosen temperature range combine full density, high transformability and small grain size. Toughness measurements by direct crack length measurements delivered unrealistically high fracture toughness values.

Keywords

• zirconia
• high toughness
• microstructure
• phase composition