Effect of different materials for temporary removable partial denture: an in vitro study on surface roughness and fracture resistance

Abstract

ABSTRACT The use of removable partial dentures is considered a common and inexpensive treatment option to rehabilitate edentulous areas. The aim of this study was to evaluate the effect of different materials for provisional removable partial dentures, an in vitro study on surface roughness and fracture resistance. Thermopolymerizable acrylic resin and thermoplastic resin specimens with dimensions of 10 x 10 x 2 mm (blocks) (n=10) and with dimensions of 65 x 20 x 3 mm (bars) (n=10 were analyzed for their surface roughness (Ra) and three-point flexural strength test. All specimens were subjected to oven aging for 60 days at 37°C±0.5°C in distilled water. The statistical analysis was performed with a significance level of 5%, and the surface roughness data were submitted to the Two-way Anova statistical test (P < 0.05) and the mechanical strength data were subjected to One-way Anova statistical test (P < 0.05). For roughness, the factor resin type (P = 0.000) and the factor aging (P = 0.000) were statically significant, as well as showing interaction (P = 0.228). The Thermopolymerizable acrylic resin had the lowest mean roughness values compared to the thermoplastic resin and showed no statistical difference after aging. The same scenario was repeated for flexural strength values; Thermopolymerizable acrylic resin was statistically superior to thermoplastic resin (P = 0.000). Thermopolymerized acrylic resin showed lower surface roughness values and higher flexural strength values compared to thermoplastic resin.

Keywords

• Dental prosthesis
• Flexural strength
• Polymers