Crystallization Kinetics of Modified Basalt Glass

Abstract

As the raw material for the production of basalt continuous fibers in Sichuan, basalt glass (BG) and modified basalt glass (MBG) were prepared by the melt quenching method with the basalt and chemically modified basalt, respectively. The crystallization kinetics of BG and MBG were investigated by differential scanning calorimetry (DSC) according to Kissinger methods. The results revealed that it is difficult for both glasses to crystallize at a high temperature. In addition, the crystallization activation energy of MBG is much higher than that of BG, which indicates that MBG is more difficult to crystallize than BG. The crystalline phases seemed to be formed from the surface of the two glasses. The morphologies and crystal structure of the crystalline phases in the heat-treated BG and MBG were analyzed by scanning electron microscope (SEM/EDX) and XRD. It was found that only a small amount of crystalline phase can be observed in the MBG, which indicates that the crystallization ability of the MBG was greatly suppressed. Results of this initial investigation indicate that chemical modification can effectively suppress the crystallization tendency of basalt glass and improve its thermal stability, which opens up an effective way for the industrial scale and stable production of basalt fiber.

Keywords

• basalt glass
• crystallization activation energy
• crystal growth index
• crystallization kinetics
• crystalline phase