Preparation and Self-Healing Properties of Clinker/PVP Microsphere in Cement Paste

Abstract

This paper presents a new insight into the autolytic mineral self-healing method for cementitious materials. The clinker/PVP (polyvinyl pyrrolidone) autolytic microsphere was prepared via the film coating method with cement clinker as a healing agent and PVP as the autolytic coating film. The morphology and chemical structure of the microsphere were characterized by environmental scanning electron microscopy (FESEM) equipped with energy dispersive spectrometer (EDS) and Fourier transform infrared spectroscopy (FTIR), respectively. The clinker retaining original mineral healing composition was successfully coated with a PVP film confirmed by FTIR. The maximum film thickness was 7.54 μm, which was determined by laser particle size measurement. The autolytic behavior was measured using isothermal calorimetry and successfully controlled by pretreatment degree (i.e., silane coupling agent amount). Experimental results showed that the compressive strength recovery of cement paste with a 30% microsphere was 54% higher than ordinary cement paste specimens. The damage degree of the specimen was also decreased by adding the autolytic microsphere.

Keywords

• autolytic mineral self-healing
• clinker
• film coating
• autolytic behavior