Phase Transitions in the Co–Al–Nb–Mo System

Abstract

Phase transitions in the Co-rich part of the Co–Al–Nb–Mo phase diagram are studied by energy dispersive spectroscopy (EDS), X-ray analysis, transmission electron microscopy (TEM), and differential scanning calorimetry (DSC) measurements. The obtained results were compared with the results for alloys of the binary Co–Al and ternary Co–Al–Nb, and Co–Al–Mo systems. Formation of the intermetallic phase with the L12 structure was found in a range of alloys with 10 at.% Al, 2–9 at.% Nb, and 3–7 at.% Mo. Intermetallic compound Co2Nb, Laves phase with the different chemical composition and crystal structure (C14 and C36) was detected in the Co–Al–Nb and Co–Al–Nb–Mo samples after vacuum solution treating at 1250 °C for 30 h.