Cerâmica (Dec 2012)
Effect of different additives on the properties of alumina-spinel castables Efeito de diferentes aditivos nas propriedades de concretos de alumina-espinélio
Abstract
Physical properties of low cement castable containing 22 wt.% Al2O3-rich MgO-Al2O3 spinel and 1.7 wt.% CaO with addition of polyacrylates, castament FS20, TPP and citric acid were investigated. Results showed castables including castament FS20 have higher flow values and better final properties comparing with castables including Darvan 7S and TPP. Also in this study we investigated the effect of addition of microsilica up to 4 wt.% on the properties of alumina-spinel castables. Microsilica is the finest particles in the system and due to suitable distribution of microsilica among other particle the open porosity reduced and mechanical strength increased. Slag penetrations resistance increased with increasing microsilica addition by forming a densification layer right behind the hot face of castables in service.As propriedades físicas de concretos de baixo cimento contendo 22 peso% Al2O3 em espinélio MgO-Al2O3 e 1,7 peso% CaO com adição de poliacrilatos, concrtagem FS20, TPP e ácido cítrico foram estudadas. Os resultados mostram que os concretos contendo FS20 tem maiores valores de fluência e melhores propriedades finais comparando com concretos como Darvan 7S e TPP. Foi também estudado o efeito da adição de microsílica até 4 peso% nas propriedades de concretos de espinélio-alumina. Microsílica é a partícula mais fina no sistema e, devido à distribuição adequada de microsílica entre as outras partículas, a porosidade aberta foi reduzida e a resistência mecânica aumentou. A resistência à penetração de escória aumentou com o aumento da adição de microsílica formando uma camada de densificação logo atrás da face quente dos concretos em uso.