A comparison of elasto-plastic parameters of S355 steel obtained in tensile tests using an extensometer, a strain gauge and an ARAMIS 3D DIC system

Abstract

The paper presents a comparison of three strain measurement methods. The mechanical parameters of S355 grade steel (yield strength, tensile strength, modulus of elasticity) were determined in tensile tests. Strains were measured using high resolution measuring instruments: an extensometer, a strain gauge and an ARAMIS 3D DIC system. In this paper, these three instruments have been used simultaneously in tensile tests for the first time. The results indicate that the values of the Young’s modulus obtained using different techniques were similar when each instrument measured strain on the same side of the sample. Small differences were connected with different gauge lengths and their locations. The values of the Young’s modulus determined on the opposite sides of the samples were more varied even when the same method was used (strain gauge measurements). For this reason, it is recommended to use double-sided averaging instruments when the Young’s modulus is determined. The strain-curves obtained from the strain gauge measurements were incomplete and they came to an end at the end of the yield plateau due to the fact that they were damaged when the values of strain were relatively high. The extensometer was used up to the point where the strain reached 0.3% and then the strain was measured based on the distance between the machine clamps. The stress-strain curves obtained from the DIC system were complete because the system was able to monitor the sample until the very end of the tests.

Keywords

• aramis
• mechanical parameters of steel
• modulus of elasticity
• tensile test
• digital image correlation