A Flexible Pressure Sensor Based on Graphene/Epoxy Resin Composite Film and Screen Printing Process

Abstract

At present, flexible pressure-sensitive materials generally have problems with weak adhesion and poor wear resistance, which easily result in friction failure when used for plantar pressure detection. In this study, a flexible pressure sensor with the advantages of a wide detection range, fast recovery, and good abrasive resistance was designed and prepared based on the screen printing process. The pressure-sensitive unit with a structural size of 5 mm× 8 mm was a functional material system due to the use of graphene and epoxy resin. The influence of the different mass ratios of the graphene and epoxy resin on the sensing properties was also studied. The test results showed that when the mass ratio of graphene to epoxy resin was 1:4, the response time and recovery time of the sensing unit were 40.8 ms and 3.7 ms, respectively, and the pressure detection range was 2.5–500 kPa. The sensor can detect dynamic pressure at 0.5 Hz, 1 Hz, 2 Hz, 10 Hz, and 20 Hz and can withstand 11,000 cycles of bending. In addition, adhesion tests showed that the high viscosity of the epoxy helped to improve the interlayer bond between the pressure-sensitive materials and the flexible substrate, which makes it more suitable for plantar pressure detection environments, where friction is common.

Keywords

• flexible pressure sensor
• graphene
• epoxy resin
• piezoresistive principle
• abrasive resistance