Investigation of the Shear Mechanical Behavior of Sandstone with Unloading Normal Stress after Freezing–Thawing Cycles

Abstract

Freezing–thawing action has a great impact on the physical and mechanical deterioration processes of rock materials in cold areas where environmental changes are very complicated. The direct shear test under unloading normal stress was adopted to investigate the shear mechanical behavior of sandstone samples after a freezing–thawing cycle in this paper. The failure shear displacement (Dsf), the failure normal displacement (Dnf), the shear displacement of unloading (Dsu), and the normal displacement of unloading (Dnu) were analyzed to describe the evolution of shear and normal deformation during the test. The results indicated that the shear displacement increased as the freezing–thawing cycle duration increased in a direct shear test under unloading normal stress. The unloading rate and the number of freezing–thawing cycles affected the failure pattern of the rock sample significantly in both the direct shear test under unloading normal stress and the direct shear test. The three-dimensional inclination angle, the distortion coefficient, and the roughness correlation coefficient of the fracture surface are dependent on the number of freezing–thawing cycles and the unloading rate. The surface average gradient mode of the fracture surface decreased as the freezing–thawing cycle times and unloading rate rose.

Keywords

• rock mechanics
• unloading normal stress
• freezing–thawing cycle
• shear and normal displacements
• failure pattern
• fracture surface roughness