Grain Refinement of Ti-15Mo-3Al-2.7Nb-0.2Si Alloy with the Rotation of TiB Whiskers by Powder Metallurgy and Canned Hot Extrusion

Abstract

In situ synthesized TiB whiskers (TiBw) reinforced Ti-15Mo-3Al-2.7Nb-0.2Si alloys were successfully manufactured by pre-sintering and canned hot extrusion via adding TiB2 powders. During pre-sintering, most TiB2 were reacted with Ti atoms to produce TiB. During extrusion, the continuous dynamic recrystallization (CDRX) of β grains was promoted with the rotation of TiBw, and CDRXed grains were strongly inhibited by TiBw with hindering dislocation motion. Eventually, the grain sizes of composites decreased obviously. Furthermore, the stress transmitted from the matrix to TiBw for strengthening in a tensile test, besides grain refinement. Meanwhile, the fractured TiBw and microcracks around them contributed to fracturing.

Keywords

• tib whiskers
• dynamic recrystallization
• grain refinement
• strengthening