Potential barrier behavior in BiCuVOX materials Comportamento da barreira de potencial em materiais BiCuVOX
Abstract
The BiMeVOX materials appear being high attractive for applications at low temperatures when the ionic conductivity is the determining parameter. The occurrence of many types substitution was confirmed for numerous Me ions, but the greatest interest have been focused on the BiCuVOX materials. The objective of this study was to image the potential barriers in BiCuVOX. The sample was sintered for 4 h at 750 °C and the results show that the high density compound can be obtained. Simultaneously, topography and electric force microscopy (EFM) images are viewed side-by-side. EFM experiments were performed and the results show the maps of the electric field distribution on the surface of BiCuVOX. The formation of potential barrier was observed and the width and intensity were measured.Materiais do tipo BiMeVOX são muito atrativos para aplicações em baixas temperaturas quando a condutividade iônica for o parâmetro determinante. A ocorrência de muitos tipos de substituições foi confirmada para numerosos íons Me, dentre os quais, existe um grande interesse no estudo de materiais BiCuVOX. O objetivo deste estudo foi realizar o imageamento das barreiras de potencial em uma amostra de material BiCuVOX. A amostra foi sinterizada 4 h a 750 °C e apresentou alta densidade. Imagens da superfície topográfica e de microscopia de força elétrica (EFM) foram obtidas simultaneamente em um microscópio de varredura por sonda. Os experimentos EFM mostraram um mapa da distribuição do campo elétrico na superfície do material BiCuVOx. A formação da barreira de potencial foi observada e tanto a largura quanto a altura foram medidas.
Keywords