Hybrid Advances (Aug 2023)
Scanning and transmission electron microscopy examinations of composite hybrid chromate and chromate phosphate conversion coatings exposed in hot 100% relative humidity environments
Abstract
Conversion coatings are sine qua non in the finishing of aluminium alloys. They may be put into service without coating of paints. However, for aesthetics in architectural applications, paint overcoat is common. Chromate phosphate coatings are relatively less toxic than chromate which gained the pride of place until recently. Thus, aluminium specimens coated with hybrid chromate/phosphate conversion coatings have been subjected to 100% relative humidity for 480 h at 313K in comparison to chromate coatings and bare aluminium. Scanning electron microscopy examination revealed that initial dried river bed morphologies on coated specimens were obliterated. The friable outer coatings collapsed into the cracks/environment leaving a relatively smooth surface after exposure. Additionally, transmission electron microscopy of sections before and after exposure revealed similar texture and morphological striations nearly parallel to each other throughout the length of the coatings to the metal/coating interface. These were not disrupted as well as the metal/coating interface which remained relatively smooth with no visible corrosion products after exposure. Thus, the coatings formed effective barrier between the substrate and the relatively harsh environment. From EDS, elemental compositions were the same albeit, spectral intensities remained relatively constant after humidity exposure regimes. The coatings are made up of either Cr, O and Al for chromate and Cr, P, O and Al for chromate/phosphate. At deliberately breached regions, the coatings prevented spread of corrosion and paint delamination over the substrates. On the other hand, bare aluminium was decorated with mounds of hydrated aluminium oxide/hydroxide after exposure as revealed in the SEM/TEM.