Influence of Alkali Metal Substitution on the Phase Transition Behavior of CsGaQ2 (Q = S, Se)

Abstract

The formation of solid solution series Cs1−xMxGaQ2-mC64 (M = K, Rb; Q = S, Se; x = 0–1) was studied by X-ray diffraction and spectroscopic methods, revealing a complete miscibility of CsGaQ2-mC64 with RbGaQ2 and KGaSe2, and a large miscibility gap with KGaS2. All solid solution members exhibit similar Raman spectra, indicating the covalent Ga-Q bonding character. The similar optical band gaps likewise further contribute to this conclusion. Up to a certain degree of substitution, these solid solutions undergo a phase transition similar to CsGaQ2-mC64. The influence of the substitution parameter x on phase transition process was investigated in situ using high-temperature X-ray powder diffraction experiments. Phase-pure solid solutions of the high-temperature polymorphs Cs1−xMxGaQ2-mC16 were obtained up to xmax(K) = 0.1 and xmax(Rb) = 0.3. The crystal structures of these new CsGaQ2-mC16 analogous high-temperature phases were refined from synchrotron diffraction data by Rietveld-refinement.

Keywords

• chalcogenogallates
• polymorphism
• solid solutions
• in situ X-ray diffraction
• synchrotron radiation
• Rietveld refinement