γ-Valerolactone as Bio-Based Solvent for Nanofiltration Membrane Preparation

Abstract

γ-Valerolactone (GVL) was selected as a renewable green solvent to prepare membranes via the process of phase inversion. Water and ethanol were screened as sustainable non-solvents to prepare membranes for nanofiltration (NF). Scanning electron microscopy was applied to check the membrane morphology, while aqueous rose Bengal (RB) and magnesium sulphate (MgSO4) feed solutions were used to screen performance. Cellulose acetate (CA), polyimide (PI), cellulose triacetate (CTA), polyethersulfone (PES) and polysulfone (PSU) membranes were fine-tuned as materials for preparation of NF-membranes, either by selecting a suitable non-solvent for phase inversion or by increasing the polymer concentration in the casting solution. The best membranes were prepared with CTA in GVL using water as non-solvent: with increasing CTA concentration (10 wt% to 17.5 wt%) in the casting solution, permeance decreased from 15.9 to 5.5 L/m2·h·bar while RB rejection remained higher than 94%. The polymer solubilities in GVL were rationalized using Hansen solubility parameters, while membrane performances and morphologies were linked to viscosity measurements and cloudpoint determination of the casting solutions to better understand the kinetic and thermodynamic aspects of the phase inversion process.

Keywords

• bio-based solvent
• green solvent
• polymer solubility
• polymeric membranes
• nanofiltration