Electrochemical Performance of Thick-Film Li(Ni_0.6Mn_0.2Co_0.2)O₂ Cathode with Hierarchic Structures and Laser Ablation

Abstract

The electrochemical performance of lithium-ion batteries is directly influenced by type of active material as well as its morphology. In order to evaluate the impact of particle morphology in thick-film electrodes, Li(Ni0.6Mn0.2Co0.2)O2 (NMC 622) cathodes with bilayer structure consisting of two different particle sizes were manufactured and electrochemically characterized in coin cells design. The hierarchical thick-film electrodes were generated by multiple casting using NMC 622 (TA) with small particle size of 6.7 µm and NMC 622 (BA) with large particle size of 12.8 µm. Besides, reference electrodes with one type of active material as well as with two type of materials established during mixing process (BT) were manufactured. The total film thickness of all hierarchical composite electrodes were kept constant at 150 µm, while the thicknesses of TA and BA were set at 1:2, 1:1, and 2:1. Meanwhile, three kinds of thin-film cathodes with 70 µm were applied to represent the state-of-the-art approach. Subsequently, ultrafast laser ablation was applied to generate groove structures inside the electrodes. The results demonstrate that cells with thin-film or thick-film cathode only containing TA, cells with bilayer electrode containing TBA 1:2, and cells with laser-structured electrodes show higher capacity at C/2 to 5C, respectively.

Keywords

• lithium-ion battery
• cathodes
• NMC 622
• multilayer
• hierarchical structure
• laser structure