An Experimental Study on the Frictional Behavior of Ultrathin Metal Sheets at Elevated Temperatures

Abstract

Hot forming is an effective approach for improving the formability of ultrathin metal sheets, such as those made of stainless steel and pure titanium. However, the increased friction coefficient between the tool and the high-temperature metal sheet negatively affects material flow during hot forming, potentially resulting in severe local thinning or even cracking. This study explores the frictional behavior of 0.1 mm thick ferritic stainless steel (FSS) and commercially pure titanium (CP-Ti) sheets at elevated temperatures. A friction testing apparatus was developed to measure the friction coefficients of these metal sheets from room temperature (25 °C) up to 600 °C. The friction coefficient of the FSS sheet increased monotonically with temperature, whereas that of the CP-Ti sheet first increased and then decreased. Post-friction testing microscopic examination demonstrated that built-up edges formed on the surfaces of the friction blocks when rubbed against the stainless steel, contributing to the higher friction coefficients. This study provides a foundation for understanding frictional behavior during the hot forming of ultrathin metal sheets.

Keywords

• ultrathin metal sheets
• high temperature
• frictional behavior
• dynamic measurement