Fabrication and Electrochemical Performance of LiNi_0.5Co_0.2Mn_0.3O₂ Coated with Nano FePO₄ as Cathode Material for Lithium-ion Batteries

Abstract

Layered LiNi0.5Co0.2Mn0.3O2 coated with homogeneous nano FePO4 suspension was prepared by using co-precipitation method. XRD, TG-DTA and TEM were adopted to characterize the structure, morphology and liquid state of FePO4 prepared. The structure, morphology and electrochemical performance of the coated materials prepared were characterized by the means such as XRD, SEM, EDS, TEM, ICP, galvanostatic charge-discharge cycling, cyclic voltammetry (CV) and electrochemical impedance spectroscopy(EIS) tests. The effect of heat treatment temperature and coating quantity on the structure and electrochemical performance of coated LiNi0.5Co0.2Mn0.3O2 by co-precipitation method was explored. The results show that 400℃ and 2%(mass fraction,the same below) FePO4 coating can significantly improve cycle performance and rate capability of LiNi0.5Co0.2Mn0.3O2, CV and EIS testing results reveal that FePO4 coating can improve the reversibility and dynamic performance for LiNi0.5Co0.2Mn0.3O2. ICP results show that FePO4 coating layer can effectively reduce the electrolyte to dissolute and erode cathode materials, stabilize its layered structure, then improve the electrochemical performance of cathode materials.

Keywords

• FePO₄
• cathode material
• LiNi_0.5Co_0.2Mn_0.3O₂
• coating modification