Synthesis of Bithiophene-Based D-A1-D-A2 Terpolymers with Different A2 Moieties for Polymer Solar Cells via Direct Arylation

Abstract

A series of bithiophene (2T)-based D-A1-D-A2 terpolymers with different A2 moieties were prepared via direct arylation reaction. In these terpolymers, pyrrolo[3,4-c]pyrrole-1,4-dione (DPP) was selected as the first electron-accepting (A1) moiety, 2,1,3-benzothiadiazole (BT) or fluorinated benzothiadiazole (FBT) or octyl-thieno[3,4-c]pyrrole-4,6-dione (TPD) or 2,1,3-benzoselendiazole (SeT) was selected as the second electron-accepting (A2) moiety, while bithiophene with hexyl side chain was used as the electron-donating moiety. The UV-vis absorption, electrochemical properties, blend film morphology, and photovoltaic properties were studied to explore the effects of the A2 moiety. It is shown that these terpolymer films exhibit broad absorption (350–1000 nm), full width at half-maximum of more than 265 nm and ordered molecular packing. Varying the A2 moiety could affect the energy levels and blend film morphology leading to different polymer solar cell (PSC) performances of these (2T)-based D-A1-D-A2 terpolymers. As a result, the highest Jsc of 10.70 mA/cm2 is achieved for Polymer 1 (P1) with BT as A2 moiety, while the higher highest occupied molecular orbital (HOMO) level limits the open circuit voltage (Voc) and leads to a power conversion efficiency (PCE) of 3.46%.

Keywords

• D-A1-D-A2 terpolymers
• direct arylation
• polymer solar cells
• pyrrolo[3,4-c]pyrrole-1,4-dione
• bithiophene