Characterization of Nanoparticles Using DSPE-PEG2000 and Soluplus

Abstract

The aim of this study was to evaluate the characterized hydration method to prepare nanoparticles using Soluplus, a block copolymer with amphipathic properties, and distearoyl phosphatidyl ethanolamine (DSPE)-PEG2000 owing to particle size distribution, zeta potential, particle stability, and transmission electron microscopy (TEM) observed and 31P-NMR spectra. The results showed that, in a suspension of DSPE-PEG2000 and Soluplus at a ratio of 1/1, the prepared microparticles were stable for five days in the dark and at 25 °C. It was also confirmed that the 1/1 suspension of DSPE-PEG2000/Soluplus was stable for five days under the same conditions with the magnesium chloride solution. TEM measurements confirmed the presence of micelle-like particles of 50 to 150 nm in the 1/1 ratio mix of DSPE-PEG2000/Soluplus. 31P-NMR spectral data confirmed that DPSE-PEG2000/Soluplus at mixing ratio of 1/1 has a strong intermolecular with the phosphate group, indicated by the fact that the peak shift and the full width at half maximum were the largest compared with DSPE-PEG2000 with the intermolecular interaction. On the basis of the findings of this study, we conclude that microparticles can be formed using DSPE-PEG2000 and Soluplus via the hydration method, and that the optimum weight ratio of DSPE-PEG2000 to Soluplus is 1/1.

Keywords

• nanoparticles
• Soluplus
• DSPE-PEG2000
• intermolecular interaction
• ³¹P-NMR