Light Absorption Enhancement and Laser-Induced Damage Ability Improvement of Aluminum Alloy 6061 with Non-Porous Alumina/CdSe@Al₂O₃/SiO₂ Functional Gradient Films

Abstract

Numerical calculations of ultraviolet to near-infrared absorption spectra by cadmium selenide quantum dots (CdSe QDs) doped in anodic aluminum oxide pores were performed using a finite-difference time-domain model. The height, diameter, and periodic spacing of the pores were optimized. Light absorption by the dots was enhanced by increasing the height and decreasing the diameter of the pores. When the height was less than 1 μm, visible light absorption was enhanced as the spacing was reduced from 400 nm to 100 nm. No enhancement was observed for heights greater than 6 μm. Finally, the optical mode coupling of the aluminum oxide and the quantum dots was enhanced by decreasing the pore diameter and periodic spacing and increasing the height. Laser ablation verified light absorption enhancement by the CdSe QDs. The experiments verified the improvement in the laser-induced damage ability with a nanosecond laser at a wavelength of 355 nm after aluminum alloy 6061 was coated with functional films and fabricated based on numerical calculations.

Keywords

• CdSe QDs
• AA 6061
• light absorption
• laser ablation