Effect of the CAD/CAM Milling Protocol on the Fracture Behavior of Zirconia Monolithic Crowns

Abstract

Although advancements in CAD/CAM technology allow for more personalized treatments, it is not clear how modifications in the CAD/CAM milling process could affect the restoration surface conditions and their mechanical behavior. The objective of this study was to evaluate the effect of different CAD/CAM milling protocols on the topography and fracture behavior of zirconia monolithic crowns (3Y-PSZ) subjected to a chewing simulation. Monolithic 3Y-PSZ premolar crowns were milled using three protocols (n = 13) (slow (S), normal (N), and fast (F)). Crowns were cemented on a dentin analog abutment and subjected to mechanical aging (200 N, 2 Hz, 1,500,000 cycles, 37 °C water). Surviving crowns were subjected to compressive load test and analyzed using fractography. Fracture load data were analyzed with two-parameter Weibull analysis. The surface topography of the crowns was examined with a stereomicroscope and a 3D non-contact profiler. All crowns survived the chewing simulation. Crowns milled using the F protocol had the greatest characteristic fracture load, while crowns produced with the S protocol showed high Weibull modulus. Groups N and S had a more uniform surface and detailed occlusal anatomy than group F. The CAD/CAM milling protocol affected the topography and mechanical behavior of 3Y-PSZ monolithic crowns.

Keywords

• CAD/CAM
• ceramics
• fixed dental prosthesis
• zirconia