Novel bricks based lightweight Vietnam's white clay minerals for gamma ray shielding purposes: An extensive experimental study

Abstract

In the present work, a new brick series based on the Vietnamese white clay minerals from the Bat Trang was fabricated to be applied in the radiation protection applications during the decommissioning of the nuclear power reactors. The bricks were constructed under various pressure rates varied from 7.61 MPa to 114.22 MPa. The influence of pressure rate on the physical and γ-ray shielding properties were investigated in the study. The experimental measurement for the material's density using the MH-300A density meter showed an enhancement in the prepared bricks' density by 22.5 % with increasing the applied pressure rate while the bricks' porosity reduced by 31.2 % when the pressure rate increased from 7.61 MPa to 114.22 MPa. The increase in the fabricated bricks density and the reduction in their porosities enhances the bricks' linear attenuation coefficients as measured by the NaI (Tl) detector along the energy range extended from 0.662 MeV to 1.332 MeV. The linear attenuation coefficient increased by 13.8 %, 17.6 %, 17.0 %, and 17.1 % at gamma ray energies of 0.662 MeV, 1.173 MeV, 1.252 MeV, and 1.332 MeV, respectively. The enhancement in the linear attenuation coefficient increases the bricks' radiation protection efficiency by 10.22 %, 14.48 %, 14.09 %, and 14.26 % at gamma ray energies of 0.662 MeV, 1.173 MeV, 1.252 MeV, and 1.332 MeV, respectively.

Keywords

• Lightweight radiation shielding materials
• White Bat Trang clay minerals
• Pressure rate
• Gamma ray protection