Improved Interface Morphology and Failure Load of Ultrasonic-Assisted Friction Stir Lap Welding Joint of 2024 Aluminum Alloy to 304 Stainless Steel

Abstract

Achieving high-strength welding joint of aluminum to steel is a highly pressing and challenging task in the manufacturing industries, and friction stir lap welding (FSLW) has advantages for joining these two metals. To further heighten the strength of dissimilar aluminum and steel metals (Al/steel) FSLW joint, the ultrasonic-assisted FSLW (UAFSLW) process was used, and the upper 2024-T4 aluminum alloy and the lower 304 stainless steel were chosen as research object. The results show that the addition of ultrasound eliminates the micro pores, changes the aluminum-rich intermetallic compounds (IMCs) into the iron-rich IMCs and enhances the micro and macro mechanical interlocking structures along the Al/steel lap interface. Under the rational IMCs layer thickness lower than 1.5 μm, the UAFSLW joint has the failure load higher than the traditional FSLW joint. The maximum failure load of UAFSLW joint reaches 7.06 kN, and the loading capacity of this joint is higher than that of reported Al/steel traditional FSLW joint. The UAFSLW process is an effective way to fabricate the high-strength Al/steel lap joint.

Keywords

• dissimilar aluminum and steel metals
• ultrasonic-assisted friction stir lap welding
• lap interface
• mechanical interlocking
• failure load