Electrochemical behavior and morphology of selected sintered samples of Mg65Zn30Ca4Pr1 alloy

Abstract

In order to investigate the effect of the milling time on the corrosion resistance of the Mg65Zn30Ca4Pr1 alloy, powders of the alloy were prepared and milled for 13, 20, and 70 hours, respectively. The samples were sintered using spark plasma sintering (SPS) technology at 350◦C and pressure of 50 MPa. The samples were subjected to potentiodynamic immersion tests in Ringer’s solution at 37◦C. The obtained values of Ecorr were –1.36, –1.35, and –1.39 V, with polarization resistance Rp = 144, 189, and 101 Ω for samples milled for 13, 20 and 70 h, respectively. The samples morphology showed cracks and pits, thus signaling pitting corrosion.

Keywords

• magnesium
• rare-earth elements
• sps
• corrosion