BMC Oral Health (Sep 2023)
Influence of long -term thermal cycling and masticatory loading simulation on bond strength of roots filled with epoxy resin and calcium silicate based sealers
Abstract
Abstract Background The aim of this study was to evaluate the effect of thermal and mechanical cyclic aging using a mastication simulator on push-out bond strength of mandibular premolars obturated with AH Plus and BioRoot RCS root canal sealers. Methods With REVO-S files up to SU/0.06 taper, 48 single-rooted premolar teeth were instrumented. The teeth were randomly divided into two main groups (n = 24) based on the two root canal sealers used (AH Plus and BioRoot RCS). All teeth were obturated with h matched-taper single-cone. Each main group was then subdivided into three subgroups (A, B, and C) (n = 8). Group A served as the negative control group (no-thermocycling aging). While groups B and C were subjected to thermal changes in a thermocycler machine (15,000 and 30,000 thermal cycles, respectively), followed by two different dynamic loading periods, 3 × 105 and 6 × 105 in a masticatory simulator with a nominal load of 5 kg at 1.2 Hz which represent roughly 1½ and 3 years of clinical function respectively. 2 mm slice at 3 levels, apical, middle, and coronal, to obtain 3 sections were prepared and subjected to push-out test using a universal testing machine. Statistical analysis was performed using analysis of variance (ANOVA) followed by a Tukey post hoc comparisons test and an independent T-test. A significance level of 5% was used. Results After thermal–mechanical cyclic aging, the two root canal sealers showed a significantly decreased in push-out bond strength (p < 0.05), however, AH Plus had significantly higher bond strength values than BioRoot RCS after cycling aging. Conclusions It could be concluded that thermal–mechanical cyclic aging had a significant impact on the outcome of the dislodgment resistance of AH Plus and BioRoot RCS.
Keywords