EFFECT OF PITCH PETROLEUM OXIDATION ON MESOPHASE PRODUCTION
Abstract
This study used two Colombian petroleum pitches (an asphalt and a precipitate) to determine their capacity as precursor of carbonaceous materials. In order to obtain the mesophase, pitches were oxidized at temperature of 350°C and oxidation times of 2; 3 and 5 hours. Oxidized pitches were fractioned with toluene using a ratio of 20 mL Toluene/g of oxidized bitumen. Insoluble material in Toluene (IT) and Tetrahydrofurane (ITHF) were carbonized with nitrogen at 400°C. For the identification of the mesophase, specimens were fabricated with the material obtained from carbonization. For the quantification of the mesophase, a microscope with polarized light filter was used. A total of 500 points were counted. The results showed that the asphalt treated with the longest oxidation time, contained higher concentration of mesophase. By contrast, the precipitate treated with the shortest oxidation time produced higher concentration of mesophase.Este trabajo usó dos breas de petróleo colombianas (un asfalto y un precipitado) con el fin de determinar su capacidad como precursor de materiales carbonosos. Para la obtención de la mesofase, las breas se oxidaron con aire a la temperatura de 350°C y a tiempos de oxidación de 2; 3 y 5 horas. Las breas oxidadas se fraccionaron con tolueno usando una razón de 20 mL Tolueno/g de brea oxidada. El material Insoluble en Tolueno (IT) y en Tetrahidrofurano (ITHF) se carbonizó en atmósfera de nitrógeno a 400°C. Para la identificación de la mesofase se fabricaron probetas con el material obtenido de carbonización. Para la cuantificación de la mesofase se utilizó un microscopio con filtro de luz polarizada. Un total de 500 puntos fueron contados. Los resultados mostraron que el asfalto presentó alta concentración de mesofase usando altos tiempos de oxidación. Por el contrario, el precipitado produjo altas concentraciones de mesofase a bajos tiempos de oxidación.Este trabalho usou dois breus de petróleo colombianos (um asfalto e um precipitado) com a finalidade de determinar a sua capacidade como precursor de materiais carbonosos. Para a obtenção da mesofase, os breus se oxidaram com ar na temperatura de 350°C e a tempos de oxidação de 2; 3 e 5 horas. Os breus oxidados se fracionaram com tolueno usando uma razão de 20 mL Tolueno/g de breu oxidado. O material Insolúvel em Tolueno (IT) e Insolúvel em Tetrahidrofurano (ITHF) se carbonizou em atmosfera de nitrogênio a 400°C. Para a identificação da mesofase se fabricaram provetas com o materia obtido de carbonização. Para a quantificação da mesofase se utilizou um microscópio com filtro de luz polarizada. Um total de 500 pontos foi contado. Os resultados mostraram que o asfalto apresentou alta concentração de mesofase usando altos tempos de oxidação. Pelo contrário, o precipitado produziu altas concentrações de mesofase a baixos tempos de oxidação.