Influence mechanism of grinding surface quality of 20CrMnTi steel on contact failure

Abstract

Abstract To reveal the influence mechanism of the grinding surface quality of 20CrMnTi steel components on the tribological characteristics and contact fatigue performance, accelerated tests for sliding friction wear and fatigue damage were carried out. Tribological characteristics and contact fatigue performance get worse with increasing surface roughness while getting better with increasing surface microhardness. Residual compressive stress is conducive to inhibiting the initiation and propagation of cracks and promoting contact fatigue performance. Additionally, mechanical friction, abrasive wear, adhesive wear and fatigue damage coexist and form a competing failure mechanism under the synergistic effect of frictional wear and contact fatigue failure. The damage process mainly manifests as wear, stress concentration induced fatigue, microcracks, pitting, and spalling in the shallow layer. This study is more beneficial to promote the 20CrMnTi steel transmission parts manufacturing products for high precision, low damage, and long life.

Keywords

• 20CrMnTi steel
• Grinding surface quality
• Tribological characteristics
• Contact fatigue