Applied Surface Science Advances (Jun 2021)
A comparative study on morphological, mechanical and tribological properties of electroless NiP, NiB and NiBP coatings
Abstract
The aim of this paper is to fabricate the NiBP polyalloys coatings by electroless coating technique on the aluminum substrate. A comparative investigation of morphological and hardness properties between NiP, NiB and NiBP coatings is employed. Also, the effect of heat treatment process on the nanoindentation behaviors of the electroless nickel-based alloys is studied. The highest hardness of 8.76 GPa and Young's modulus of 180.36 GPa were obtained electroless NiBP coatings in the case of as-plated conditions. After heat treatment process at 400°C in an inert atmosphere, electroless NiB coatings showed the highest hardness value of 10.02 GPa and Young's modulus of 207.48 GPa when compared with NiP and NiBP coatings. Although electroless NiB coatings exhibited the highest Young's modulus and harness value, electroless NiBP coatings showed the best protection against wear in all loads of 1, 2 and 3N and all sliding velocities of 100, 200 and 400 mm/s due to showing H/E ratio of NiBP coatings comparing with NiB and NiP coatings.