Boletín de la Sociedad Española de Cerámica y Vidrio (Aug 2005)
Comportamiento en fatiga de cintas superconductoras multifilamento BSCCO 2223
Abstract
The mechanical properties and the critical current were studied in three commercial multi-filamentary BSCCO 2223 tapes (formed by Bi2Sr2Ca2Cu3O10+x high-temperature ceramic superconductors embedded in a Ag-Mg alloy) subjected to monotonic and fatigue tension at 77 K in the longitudinal direction. It was found that transport properties were not comprised under monotonic tensions if the maximum tensile stress remained below the conventional 0.2% yield strength. This magnitude was reduced by 10% to 20% in the case of fatigue loading, and the service life of the tape was dictated by the mechanical fatigue life.<br><br>Las propiedades mecánicas y la evolución de la corriente crítica durante una solicitación mecánica han sido evaluadas en tres cintas comerciales multifilamento formadas por una aleación Ag-Mg reforzada con fibras superconductoras cerámicas de alta temperatura crítica Bi2Sr2Ca2Cu3O10+x (denominadas cintas BSCCO 2223). Estas cintas fueron sometidas a una solicitación monótona creciente y a fatiga mecánica a 77 K a lo largo de la dirección longitudinal. Los resultados obtenidos revelan que las propiedades de transporte eléctrico no se ven afectadas bajo tensiones monótonas crecientes si la tensión máxima a tracción es inferior al límite elástico de la cinta definido a partir del 0.2% de deformación ingenieril. Sin embargo, la corriente crítica se reduce entre un 10% y 20% bajo una solicitación cíclica, lo que indica que la vida en servicio de estas cintas está condicionada por su comportamiento bajo fatiga mecánica.