Boletín de la Sociedad Española de Cerámica y Vidrio (Jun 1999)
Catalizadores MnO<sub>x</sub>-TiO<sub>2</sub> para la eliminación de compuestos orgánicos volátiles
Abstract
Mn-Ti mixed oxides with stoichiometry TixMn1-xOy (with x = 0, 0.1, 0.2, 0.5, 0.8, 0.9, 1) have been prepared by a coprecipitation method. Mn3O4 (hausmannite) and TiO2 (anatase) were found to be the main crystalline phases, while solid solutions appeared to be formed at the extreme values of x. Thermal stability of these materials reaches 873 K, transforming into thermodynamically stable phases, TiO2 (rutile) y α-Mn2O3, at higher temperatures. From catalytic point of view, they are active in propane and propene oxidation, though the increase of Ti content seems to deactivate Mn oxide for propene oxidation. Conversely, the sample with the Mn/Ti = 1 ratio presents a maximum for propane oxidation.Se han sintetizado muestras de Mn-Ti de fórmula general TixMn1-xOy (x = 0, 0.1, 0.2, 0.5, 0.8, 0.9, 1) mediante un método de coprecipitación. Las fases cristalinas mayoritarias identificadas fueron Mn3O4 (hausmanita) y TiO2 (anatasa), formándose también disoluciones sólidas a bajos porcentajes de uno de los cationes. Los materiales son estables térmicamente hasta los 873 K, tranformándose en las fases termodinámicamente estables, TiO2 (rutilo) y α-Mn2O3 a mayores temperaturas. Desde el punto de vista catalítico, son activos en la oxidación de propano y propeno, aunque el aumento del contenido de Ti parece desactivar el óxido de Mn en la oxidación de propileno. Contrariamente, en la oxidación de propano la relación Mn/Ti=1 presenta un máximo en la conversión de propano.