Extrusion-Based 3D Printing of CuSn10 Bronze Parts: Production and Characterization

Abstract

The interest in producing cost-effective 3D printed metallic materials is increasing day by day. One of these methods, which has gained much attention recently, is the fused deposition modelling (FDM) method. The parameters used in the FDM method have significant effects on the printed part properties. In this study, CuSn10 bronze alloy was successfully produced. The printing speed and layer thickness were investigated as the printing process parameters, and their effect on morphological properties was characterized by using SEM. As a result, it was observed that the formation of printing-induced voids was prevented by applying a layer thickness of 0.2 mm. Additionally, by increasing printing speed, a slight decrease in product density was observed. Following determination of 3D printing parameters which give the highest printed part density, the parts were debound in hexane solution via solvent debinding. Finally, the parts were sintered at 850, 875 and 900 °C for 5 h to examine effect of sintering temperature on density, porosity, shape deformation and mechanical properties. Although partial slumping started to form over 875 °C, the highest density (94.19% of theoretical density) and strength (212 ± 17.72 MPa) were obtained by using 900 °C as the sintering temperature.

Keywords

• 3D printing
• sintering
• CuSn10
• mechanical properties
• characterization