Comparing the Effect of Zirconia Surface Conditioning Using Nd:YAG Laser and Conventional Method on Shear Bond Strength of Ceramic Brackets to Zirconia Surface: An In vitro Study

Abstract

Background and purpose: Lasers are of great importance in dentistry and have shown positive results in surface conditioning of ceramic brackets. The aim of this study was to compare the effect of two surface conditioning method, Nd:YAG laser and sandblasting on shear bind strength (SBS) and (adhesive remnant index (ARI). Materials and methods: This experimental study was conducted in six groups of zirconia blocks to get prepared by laser (LG1-LG2-LG3) or sandblast (SG4-SG5-SG6). Two debonding methods, including conventional (LG3-SG3) and Nd:YAG laser (LG2-SG2) methods were used for zirconia blocks. SBS and ARI indices were compared between the two methods using ANOVA and post-hoc test. Results: The mean SBS did not show significant difference between LG1 and SG4 groups (8.2±2.04 and 7.1±1.5, respectively, P=0.228). ARI did not show significant difference between LG2 (3.1±0.8) and SG5 (3.5±0.7) groups (P=0.129) and between LG3 and SG6 (2.3±0.7 and 2.7±0.5, respectively, P=0.219). ARI was found to be significantly different between LG2 and LG3 (30.1±0.8 and 2.3±0.7, respectively, P =0.011) and between SG5 (3.5±0.7) and SG6 (2.7± 0.5) (P=0.024). Conclusion: Nd:YAG laser can be considered a suitable alternative for zirconia surface conditioning and debonding ceramic brackets from zirconia crowns.

Keywords

• laser
• sandblast
• zirconia
• zirconia
• shear bond strength