Microstructural, Mechanical, and Electrochemical Characterization of CrMoNbTiZr High-Entropy Alloy for Biomedical Application

Abstract

High-entropy alloys (HEA) with superior biocompatibility, high pitting resistance, minimal debris accumulation, and reduced release of metallic ions into surrounding tissues are potential replacements for traditional metallic bio-implants. A novel equiatomic HEA based on biocompatible metals, CrMoNbTiZr, was consolidated by spark plasma sintering (SPS). The relative sintered density of the alloy was about 97% of the theoretical density, indicating the suitability of the SPS technique to produce relatively dense material. The microstructure of the sintered HEA consisted of a BCC matrix and Laves phase, corresponding to the prediction of the thermodynamic CALPHAD simulation. The HEA exhibited a global Vickers microhardness of 531.5 ± 99.7 HV, while the individual BCC and Laves phases had hardness values of 364.6 ± 99.4 and 641.8 ± 63.0 HV, respectively. Its ultimate compressive and compressive yield strengths were 1235.7 ± 42.8 MPa and 1110.8 ± 78.6 MPa, respectively. The elasticity modulus of 34.9 ± 2.9 GPa of the HEA alloy was well within the range of cortical bone and significantly lower than the values reported for commonly used biomaterials made from Ti-based and Cr–Co-based alloys. In addition, the alloy exhibited good resistance to bio-corrosion in PBS and Hanks solutions. The CrMoNbTiZr HEA exhibited an average COF of 0.43 ± 0.06, characterized mainly by abrasive and adhesive wear mechanisms. The CrMoNbTiZr alloy’s mechanical, bio-corrosion, and wear resistance properties developed in this study showed a good propensity for application as a biomaterial.

Keywords

• high-entropy alloy
• biomaterials
• CrMoNbTiZr
• powder methods
• bio-corrosion