Experimental Investigation of Methyl Methacrylate in Stirred Batch Emulsion Reactor: AGET ATRP Approach

Abstract

This study examines the ab initio emulsion atom transfer radical polymerization (ATRP) initiated by an eco-friendly reducing agent to produce poly(methyl methacrylate) (PMMA) polymer with controlled characteristics in a 2 L stirred batch reactor. The effect of the reaction temperature, surfactant concentration, monomer to water ratio, and stirring speed was thoroughly investigated. The results showed that PMMA coagulation becomes quite severe at a certain temperature threshold. However, the coagulation could be avoided at mild reaction temperature, since the outcomes showed that loading more surfactant to the system under high mixing speed has balanced the polymer mixture and yielded high monomer conversion. The PMMA product was analyzed by gravimetry and GPC measurements and after 5 h of polymerization at a reaction temperature of 50 °C, monomer conversion of 64.1% was obtained, and PMMA polymer samples produced had an average molar mass of 4.5 kg/mol and a polydispersity index of 1.17. The structure of the PMMA polymer was successfully proved by FTIR and nuclear magnetic resonance (NMR) spectroscopy. The results confirm the living feature of MMA AGET ATRP in emulsion medium and recommend further investigation for other types of surfactant.

Keywords

• AGET ATRP
• ascorbic acid
• batch reactor
• MMA
• two-step emulsion