The Influence of Zeolitic By-Product Containing Ammonium Ions on Properties of Hardened Cement Paste

Abstract

Fluid catalytic cracking (FCC) catalysts, used in the petroleum industry, are sources of zeolitic by-products. These by-products are often used as sorbents for the removal of ammonium ions from wastewater. After a period of use, the zeolitic by-product loses its sorption properties and is no longer effective. The problem is the use of zeolitic by-product with ammonium ions. In this study, a zeolitic by-product containing ammonium ions and high contents of active SiO2 and Al2O3 was used as a supplementary cementitious material (SCM). Cement pastes containing 0.5%, 1%, 3%, 5%, and 10% of the by-product were prepared, and the compressive strength and density of the pastes were evaluated. Incorporation of the zeolitic by-product increased the cement strength by 17% and 32% after 7 and 28 days of hydration, respectively. Thus, incorporation of the zeolitic by-product with ammonium ions as an SCM has a complex effect on an ordinary Portland cement (OPC) system. Ammonium chloride accelerated cement setting after 7 days of hydration, and the pozzolanic reaction positively affected strength development after 28 days of hydration. The reaction products caused the cement to have a compact microstructure. The zeolitic by-product containing absorbed ammonium ions can be successfully reused to replace ordinary Portland cement in cement pastes.

Keywords

• fluid catalytic cracking (FCC) catalysts
• zeolitic by-product
• Portland cement hydration