Probabilistic analysis of climate change impact on chloride-induced deterioration of reinforced concrete considering Nordic climate

Abstract

Abstract The impact of climate change on the deterioration of reinforced concrete elements have been frequently highlighted as worthy of investigation. This article addresses this important issue by presenting a time-variant reliability analysis to assess the effect of climate change on four limit states; the probabilities of corrosion initiation, crack initiation, severe cracking, and failure of a simply supported beam built in 2020 and exposed to chloride-induced corrosion. The historical and future climate conditions (as projected by three different emission scenarios) for different climate zones in Sweden are considered, including subarctic conditions where the impact of climate change may lead to large increases in temperature. The probabilities of all limit states are found to be: 1) higher for scenarios with higher GHG emissions and 2) higher for southern than for northern climate zones. However, the end-of-century impact of climate change on the probabilities of reaching the different limit states is found to be higher for northern than for southern climate zones. At 2100, the impact of climate change on the probability of failure can reach up to an increase of 123% for the northernmost zone. It is also noted that the end-of-century impact on the probability of failure is significantly higher (ranging from 3.5–4.9 times higher) than on the other limit states in all climate scenarios.

Keywords

• Climate change
• Infrastructure deterioration
• Reinforcement corrosion
• Monte Carlo simulation