Association of Nd:YAG laser and calcium-phosphate desensitizing pastes on dentin permeability and tubule occlusion

Abstract

Abstract Objective To evaluate the efficacy of Nd:YAG laser associated with calcium-phosphate desensitizing pastes on dentin permeability and tubule occlusion after erosive/abrasive challenges. Methodology Dentin specimens were exposed to 17% ethylene diamine tetra-acetic acid (EDTA) solution for 5 min and randomly allocated into five groups: G1, control (no treatment); G2, Nd:YAG laser (1 W, 10 Hz, 100 mJ, 85 J/cm2); G3, Laser + TeethmateTM Desensitizer; G4, Laser + Desensibilize Nano P; and G5, Laser+Nupro®. Specimens underwent a 5-day erosion-abrasion cycling. Hydraulic conductance was measured post-EDTA, post-treatment, and post-cycling. Post-treatment and post-cycling permeability (%Lp) was calculated based on post-EDTA measurements, considered 100%. Open dentin tubules (ODT) were calculated at the abovementioned experimental moments using scanning electron microscopy and ImageJ software (n=10). Data were analyzed using two-way repeated measures ANOVA and Tukey’s test (α=0.05). Results G1 presented the highest %Lp post-treatment of all groups (p0.05). We found no significant differences in ODT among groups (p>0.05) post-EDTA. At post-treatment, treated groups did not differ from each other, but presented lower ODT than G1 (p0.05), although ODT was significantly lower for all groups when compared to post-EDTA values (p<0.001). Conclusion All treatments effectively reduced dentin permeability and promoted tubule occlusion after application. Combining Nd YAG laser with calcium-phosphate pastes did not improve the laser effect. After erosive-abrasive challenges, treatments presented no differences when compared to the control.

Keywords

• Dentin hypersensitivity
• Laser
• Desensitizing agents