The existing forms of Zr in Mg-Zn-Zr magnesium alloys and its grain refinement mechanism

Abstract

The formation of the Zr-containing phases during the solidification of Mg-Zn-Zr alloy is simulated, the structure of the Zr-containing compounds and the solid solution amount of Zr in α -Mg solid solution as well as the grain size of the as-cast alloy are measured. Based on this, the existing form of Zr element in Mg-Zn-Zr alloy and its action mechanism of grain refinement are discussed. The results show that either α -Zr or α -Mg solid solution precipitates first from melt of Mg-Zn-Zr alloy at the beginning of solidification due to the different Zr content, then some Zn-Zr phases with different Zn/Zr atomic ratios form in the alloy melt during solidification. The Zr element in Mg-Zn-Zr alloy mainly exists in the form of compounds, its solid solution amount in α -Mg is not large and is inhibited by Zn element. The Zr in Mg-Zn-Zr alloy has the effect to refine grain, the reason is that the α -Zr phase and α -Mg formed by peritectic reaction or α -Mg formed from Zr atomic clusters can be used as the nucleus of subsequent α -Mg crystals. In addition, the Zr-containing compound formed during solidification can prevent the growth of grains, the enrichment of Zr in the crystallization front can also promote nucleation by component undercooling.

Keywords

• Zr element
• Mg-Zn-Zr magnesium alloy
• Zr-containing phase
• grain refinement
• solidification process