Decomposition of the β phase at intermediate temperature in β-metastable Ti-5553 alloy

Abstract

The present contribution focuses on the nature of the β → α transformation in Ti-5333 alloy at intermediate temperatures. It is indeed still unclear whether this transformation is only controlled by bulk diffusion or whether interfacial kinetics may play a role. To address this issue, we have combined SEM and STEM-EDX to measure the concentrations of Al, Cr, Mo, V and Fe in α intragranular precipitates as well as in the abutting β matrix, paying a particular attention to the concentrations at flat interfaces corresponding to the precipitates habit planes. The comparison with Calphad calculations suggests that interfaces are not at equilibrium during the thickening of the plates.

Keywords

• ti-5553 alloy
• phase transformation kinetics
• stem-edx analysis
• α/β interfaces